LG ABS AF312C
丙烯腈丁二烯苯乙烯
產(chǎn)品說(shuō)明:
Description
Application
-
Electric parts, IT/OA device
|
材料狀態(tài)
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL 黃卡
|
|
|
供貨地區(qū)
|
|
|
特性
|
|
|
用途
|
|
|
RoHS 合規(guī)性
|
|
|
加工方法
|
|
|
密度 / 比重
|
1.18
|
|
ASTM D792
|
|
熔流率（熔體流動(dòng)速率） (220°C/10.0 kg)
|
60
|
g/10 min
|
ASTM D1238
|
|
收縮率 - 流動(dòng) (73°F, 0.126 in, 注塑)
|
4.0E-3 到 7.0E-3
|
in/in
|
ASTM D955
|
|
洛氏硬度 (R 級(jí), 73°F, 注塑)
|
104
|
|
ASTM D785
|
|
拉伸模量 3 (73°F, 0.126 in, 注塑)
|
313000
|
psi
|
ASTM D638
|
|
抗張強(qiáng)度 4 (屈服, 73°F, 0.126 in, 注塑)
|
6260
|
psi
|
ASTM D638
|
|
伸長(zhǎng)率 4
|
|
|
ASTM D638
|
|
屈服, 73°F, 0.126 in, 注塑
|
5.0
|
%
|
|
|
斷裂, 73°F, 0.126 in, 注塑
|
> 20
|
%
|
|
|
彎曲模量 5 (73°F, 0.252 in, 注塑)
|
370000
|
psi
|
ASTM D790
|
|
彎曲強(qiáng)度 5 (73°F, 0.252 in, 注塑)
|
9960
|
psi
|
ASTM D790
|
|
懸壁梁缺口沖擊強(qiáng)度
|
|
|
ASTM D256
|
|
-22°F, 0.126 in, 注塑
|
1.5
|
ft·lb/in
|
|
|
-22°F, 0.252 in
|
1.5
|
ft·lb/in
|
|
|
73°F, 0.126 in, 注塑
|
5.0
|
ft·lb/in
|
|
|
73°F, 0.252 in, 注塑
|
4.2
|
ft·lb/in
|
|
|
載荷下熱變形溫度
|
|
|
ASTM D648
|
|
66 psi, 未退火, 0.252 in, 注塑
|
183
|
°F
|
|
|
264 psi, 未退火, 0.252 in, 注塑
|
171
|
°F
|
|
|
維卡軟化溫度
|
183
|
°F
|
ASTM D1525 6
|
|
RTI Elec
|
176
|
°F
|
UL 746
|
|
RTI Imp
|
158
|
°F
|
UL 746
|
|
RTI
|
176
|
°F
|
UL 746
|
|
UL 阻燃等級(jí)
|
|
|
UL 94
|
|
0.10 in
|
V-0
|
|
|
|
0.12 in
|
V-0
|
|
|
|
干燥溫度
|
176 到 194
|
°F
|
|
|
干燥時(shí)間
|
3.0 到 4.0
|
hr
|
|
|
料筒后部溫度
|
338 到 374
|
°F
|
|
|
料筒中部溫度
|
356 到 392
|
°F
|
|
|
料筒前部溫度
|
374 到 410
|
°F
|
|
|
射嘴溫度
|
392 到 446
|
°F
|
|
|
加工（熔體）溫度
|
392 到 446
|
°F
|
|
|
模具溫度
|
104 到 140
|
°F
|
|
|
背壓
|
71.1 到 142
|
psi
|
|
|
螺桿轉(zhuǎn)速
|
30 到 60
|
rpm
|
|
|