LEXAN?
243R resin
聚碳酸酯
產品說明:
10.5 MFR. UV-stabilized. Improved flame retardance. Internal mold
release.
|
材料狀態
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區
|
|
|
添加劑
|
|
|
特性
|
|
|
加工方法
|
|
|
比重
|
|
|
ASTM
D792
|
|
--
|
1.20
|
g/cm?
|
|
|
--
|
1.19
|
g/cm?
|
|
|
特定體積
|
0.830
|
cm?/g
|
ASTM
D792
|
|
熔流率（熔體流動速率） (300°C/1.2
kg)
|
11
|
g/10 min
|
ASTM
D1238
|
|
收縮率 - 流動 (3.20 mm)
|
0.50 到 0.70
|
%
|
內部方法
|
|
吸水率
|
|
|
ASTM
D570
|
|
24
hr
|
0.15
|
%
|
|
|
平衡,
23°C
|
0.35
|
%
|
|
|
平衡,
100°C
|
0.58
|
%
|
|
|
室外適用性
|
f1
|
|
UL
746C
|
|
洛氏硬度
|
|
|
ASTM
D785
|
|
M
級
|
70
|
|
|
|
R
級
|
118
|
|
|
|
抗張強度 3
|
|
|
ASTM
D638
|
|
屈服
|
62.1
|
MPa
|
|
|
斷裂
|
65.5
|
MPa
|
|
|
伸長率 3
|
|
|
ASTM
D638
|
|
屈服
|
7.0
|
%
|
|
|
斷裂
|
110
|
%
|
|
|
彎曲模量 4 (50.0 mm 跨距)
|
2340
|
MPa
|
ASTM
D790
|
|
彎曲強度 4 (屈服, 50.0 mm
跨距)
|
93.1
|
MPa
|
ASTM
D790
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
轉輪)
|
10.0
|
mg
|
ASTM
D1044
|
|
懸壁梁缺口沖擊強度 (23°C)
|
800
|
J/m
|
ASTM
D256
|
|
無缺口懸臂梁沖擊 (23°C)
|
3200
|
J/m
|
ASTM
D4812
|
|
落錘沖擊 (23°C)
|
169
|
J
|
ASTM
D3029
|
|
拉伸沖擊強度 5
|
546
|
kJ/m?
|
ASTM
D1822
|
|
載荷下熱變形溫度
|
|
|
ASTM
D648
|
|
0.45 MPa,
未退火, 6.40 mm
|
138
|
°C
|
|
|
1.8 MPa,
未退火, 6.40 mm
|
132
|
°C
|
|
|
維卡軟化溫度
|
154
|
°C
|
ASTM
D1525 6
|
|
線形熱膨脹系數 - 流動 (-40 到 95°C)
|
6.8E-5
|
cm/cm/°C
|
ASTM
E831
|
|
比熱
|
1260
|
J/kg/°C
|
ASTM
C351
|
|
導熱系數
|
0.27
|
W/m/K
|
ASTM
C177
|
|
RTI Elec
|
130
|
°C
|
UL
746
|
|
RTI Imp
|
130
|
°C
|
UL
746
|
|
RTI
|
130
|
°C
|
UL
746
|
|
體積電阻率
|
> 1.0E+17
|
ohm·cm
|
ASTM
D257
|
|
介電強度 (3.20 mm, in
Air)
|
15
|
kV/mm
|
ASTM
D149
|
|
介電常數
|
|
|
ASTM
D150
|
|
50
Hz
|
3.17
|
|
|
|
60
Hz
|
3.17
|
|
|
|
1
MHz
|
2.96
|
|
|
|
耗散因數
|
|
|
ASTM
D150
|
|
50
Hz
|
9.0E-4
|
|
|
|
60
Hz
|
9.0E-4
|
|
|
|
1
MHz
|
0.010
|
|
|
|
相比耐漏電起痕指數(CTI)
|
PLC 2
|
|
UL
746
|
|
高電弧燃燒指數(HAI)
|
PLC 1
|
|
UL
746
|
|
高電壓電弧起痕速率 (HVTR)
|
PLC 2
|
|
UL
746
|
|
熱絲引燃 (HWI)
|
PLC 4
|
|
UL
746
|
|
UL 阻燃等級
|
|
|
UL
94
|
|
0.750
mm
|
V-2
|
|
|
|
6.00
mm
|
V-0
|
|
|
|
極限氧指數
|
25
|
%
|
ASTM
D2863
|
|
折射率
|
1.586
|
|
ASTM
D542
|
|
透射率 (2540 ?m)
|
88.0
|
%
|
ASTM
D1003
|
|
霧度 (2540
?m)
|
1.0
|
%
|
ASTM
D1003
|
|
干燥溫度
|
121
|
°C
|
|
|
干燥時間
|
3.0 到 4.0
|
hr
|
|
|
干燥時間，最大
|
48
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
建議注射量
|
40 到 60
|
%
|
|
|
料筒后部溫度
|
271 到 293
|
°C
|
|
|
料筒中部溫度
|
282 到 304
|
°C
|
|
|
料筒前部溫度
|
293 到 316
|
°C
|
|
|
射嘴溫度
|
288 到 310
|
°C
|
|
|
加工（熔體）溫度
|
293 到 316
|
°C
|
|
|
模具溫度
|
71.1 到 93.3
|
°C
|
|
|
背壓
|
0.345 到 0.689
|
MPa
|
|
|
螺桿轉速
|
40 到 70
|
rpm
|
|
|
排氣孔深度
|
0.025 到 0.076
|
mm
|
|