LEXAN?
164R resin
聚碳酸酯
產品說明:
Medium viscosity, multi purpose polycarbonate resin with added release
agent. FDA food contact compliant in limited colors.Effective January 15th, 2007
this grade will no longer be supported with biocompatibility information and
should not be used for medical applications which require biocompatibility.
Alternative grade HP4REU.
|
材料狀態
|
|
|
資料 1
|
|
|
UL 黃卡 2
|
|
|
搜索 UL
黃卡
|
|
|
供貨地區
|
|
|
添加劑
|
|
|
特性
|
|
|
機構評級
|
|
|
RoHS 合規性
|
|
|
外觀
|
|
|
加工方法
|
|
|
密度
|
1.20
|
g/cm?
|
ISO
1183
|
|
溶化體積流率（MVR） (300°C/1.2
kg)
|
9.50
|
cm?/10min
|
ISO
1133
|
|
收縮率 - 流動 3
|
0.50 到 0.70
|
%
|
內部方法
|
|
吸水率
|
|
|
ISO
62
|
|
飽和,
23°C
|
0.35
|
%
|
|
|
平衡, 23°C,
50% RH
|
0.15
|
%
|
|
|
球壓硬度 (H 358/30)
|
95.0
|
MPa
|
ISO
2039-1
|
|
拉伸模量
|
2350
|
MPa
|
ISO
527-2/1
|
|
拉伸應力
|
|
|
ISO
527-2/50
|
|
屈服
|
63.0
|
MPa
|
|
|
斷裂
|
70.0
|
MPa
|
|
|
拉伸應變
|
|
|
ISO
527-2/50
|
|
屈服
|
6.0
|
%
|
|
|
斷裂
|
120
|
%
|
|
|
彎曲模量 4
|
2300
|
MPa
|
ISO
178
|
|
彎曲應力 4, 5
|
90.0
|
MPa
|
ISO
178
|
|
泰伯耐磨性 (1000 Cycles, 1000 g, CS-17
轉輪)
|
10.0
|
mg
|
內部方法
|
|
簡支梁缺口沖擊強度
|
|
|
|
|
-30°C 6
|
14
|
kJ/m?
|
ISO
179/1eA
|
|
23°C 6
|
73
|
kJ/m?
|
ISO
179/1eA
|
|
23°C
|
35
|
kJ/m?
|
ISO
179/2C
|
|
簡支梁無缺口沖擊強度 6
|
|
|
ISO
179/1eU
|
|
-30°C
|
無斷裂
|
|
|
|
23°C
|
無斷裂
|
|
|
|
懸壁梁缺口沖擊強度 7
|
|
|
ISO
180/1A
|
|
-30°C
|
12
|
kJ/m?
|
|
|
23°C
|
70
|
kJ/m?
|
|
|
無缺口伊佐德沖擊強度 7
|
|
|
ISO
180/1U
|
|
-30°C
|
無斷裂
|
|
|
|
23°C
|
無斷裂
|
|
|
|
熱變形溫度 8
|
|
|
|
|
0.45 MPa,
未退火, 100 mm 跨距
|
138
|
°C
|
ISO
75-2/Be
|
|
1.8 MPa,
未退火, 100 mm 跨距
|
127
|
°C
|
ISO
75-2/Ae
|
|
維卡軟化溫度
|
|
|
|
|
--
|
143
|
°C
|
ISO
306/B50
|
|
--
|
145
|
°C
|
ISO
306/B120
|
|
Ball Pressure Test
|
|
|
IEC
60695-10-2
|
|
125°C
|
Pass
|
|
|
|
140°C 9
|
Pass
|
|
|
|
線形熱膨脹系數 - 流動 (23 到 80°C)
|
7.0E-5
|
cm/cm/°C
|
ISO
11359-2
|
|
導熱系數
|
0.20
|
W/m/K
|
ISO
8302
|
|
RTI Elec
|
130
|
°C
|
UL
746
|
|
RTI Imp
|
125
|
°C
|
UL
746
|
|
RTI
|
125
|
°C
|
UL
746
|
|
表面電阻率
|
> 1.0E+15
|
ohm
|
IEC
60093
|
|
體積電阻率
|
> 1.0E+15
|
ohm·cm
|
IEC
60093
|
|
介電強度 (3.20 mm,
在油中)
|
17
|
kV/mm
|
IEC
60243-1
|
|
相對電容率
|
|
|
IEC
60250
|
|
50
Hz
|
2.70
|
|
|
|
60
Hz
|
2.70
|
|
|
|
1
MHz
|
2.70
|
|
|
|
耗散因數
|
|
|
IEC
60250
|
|
50
Hz
|
1.0E-3
|
|
|
|
60
Hz
|
1.0E-3
|
|
|
|
1
MHz
|
0.010
|
|
|
|
UL 阻燃等級
|
|
|
UL
94
|
|
1.50
mm
|
HB
|
|
|
|
3.00
mm
|
HB
|
|
|
|
灼熱絲易燃指數 (1.00 mm)
|
850
|
°C
|
IEC
60695-2-12
|
|
極限氧指數
|
25
|
%
|
ISO
4589-2
|
|
折射率
|
1.586
|
|
ISO
489
|
|
透射率 (2540 ?m)
|
88.0 到 90.0
|
%
|
ASTM
D1003
|
|
霧度 (2540
?m)
|
< 0.80
|
%
|
ASTM
D1003
|
|
干燥溫度
|
120
|
°C
|
|
|
干燥時間
|
2.0 到 4.0
|
hr
|
|
|
建議的最大水分含量
|
0.020
|
%
|
|
|
料斗溫度
|
60.0 到 80.0
|
°C
|
|
|
料筒后部溫度
|
260 到 280
|
°C
|
|
|
料筒中部溫度
|
270 到 290
|
°C
|
|
|
料筒前部溫度
|
280 到 310
|
°C
|
|
|
射嘴溫度
|
270 到 290
|
°C
|
|
|
加工（熔體）溫度
|
280 到 310
|
°C
|
|
|
模具溫度
|
80.0 到 110
|
°C
|
|