OK 85.58是適用于熱作工具、熱修整工具、沖床等維修性焊接的耐磨堆焊焊條。焊縫金屬硬度可通過淬火及回火或僅僅回火方式得到提升。焊縫金屬可接受分級淬火。為避免開裂，預熱溫度及層間溫度應至少為300°C，推薦達到500°C。
焊縫金屬分析
|
Mn
|
C
|
Nb
|
Si
|
W
|
Co
|
Cr
|
|
0.9 %
|
0.32 %
|
0.8 %
|
1.1 %
|
7.9 %
|
2.1 %
|
1.8 %
|
熔敷數據
|
Fusion time per electrode at 90% I max
|
kg weld metal/kg electrodes
|
Number of electrodes/kg weld metal
|
安培
|
熔敷率
|
電壓 V
|
直徑
|
|
53 sec
|
0.65 kg
|
72
|
70-110 A
|
0.9 kg/h
|
22 V
|
2.5 x 350 mm
|
|
62 sec
|
0.63 kg
|
45
|
100-150 A
|
1.3 kg/h
|
23 V
|
3.2 x 350 mm
|
|
75 sec
|
0.63 kg
|
30
|
130-190 A
|
1.7 kg/h
|
23 V
|
4.0 x 350 mm
|
|
88 sec
|
0.66 kg
|
18
|
180-250 A
|
2.2 kg/h
|
25 V
|
5.0 x 350 mm
|
|
Coating Type:
|
Lime Basic
|
|
Welding Current:
|
AC, DC+
|
|
合金類型:
|
High speed steel
|
|