Austenitic manganese steel electrode with nickel for surfacing and building up mangnese steel components exposed to severe impact and moderate abrasion. The weld metal is less prone to embrittlement and cracking compared to plain austenitic manganese steel weld metal. Applications include: crusher plates and rolls, cones and mantels of rotary crushers, rail points.
典型拉伸性能
|
As welded
|
|
保護氣體
|
屈服強度
|
延伸率
|
抗拉強度
|
|
ISO
|
440 MPa
|
30 %
|
690 MPa
|
夏比V型缺口沖擊性能
|
As welded
|
|
保護氣體
|
沖擊值
|
測試溫度
|
|
ISO
|
100 J
|
20 °C
|
|
ISO
|
80 J
|
-20 °C
|
|
ISO
|
45 J
|
-80 °C
|
|
ISO
|
25 J
|
-120 °C
|
焊縫金屬分析
|
Mn
|
C
|
Si
|
Ni
|
|
13.2 %
|
0.67 %
|
0.2 %
|
3.0 %
|
熔敷數據
|
Fusion time per electrode at 90% I max
|
kg weld metal/kg electrodes
|
Number of electrodes/kg weld metal
|
安培
|
熔敷率
|
電壓 V
|
直徑
|
|
90 sec
|
0.54 kg
|
27
|
100-160 A
|
1.5 kg/h
|
30 V
|
3.2 x 450 mm
|
|
105 sec
|
0.54 kg
|
18
|
130-210 A
|
2.0 kg/h
|
30 V
|
4.0 x 450 mm
|
|
114 sec
|
0.56 kg
|
11
|
170-300 A
|
2.9 kg/h
|
31 V
|
5.0 x 450 mm
|
|
認證:
|
CE, 82.039.08, DB
|
|
分類:
|
E Z Fe9, EN 14700
|
認證均基于工廠的所在地。如需更多信息，請聯系伊薩。
|
Coating Type:
|
Zircon Basic
|
|
Welding Current:
|
AC, DC+
|
|
合金類型:
|
Austenitic Mn steel
|
|
在線咨詢 