LCP/美國杜邦/6330 阻燃級 增強(qiáng)級 耐候 高抗沖
發(fā)布者：上海韜盛塑化科技有限公司 發(fā)布時間：2023-02-13 14:07:59
物理性能額定值單位測試方法比重1.64
ASTM D-792模具收縮率 (3.2mm(0.126in))0.5%ASTM D-955機(jī)械性能額定值單位測試方法彎曲強(qiáng)度(3.2mm(0.125in),23℃(73℉))125MPaASTM D-790斷裂伸長率(3.2mm(0.125in),23℃(73℉))4%ASTM D-638彎曲模量
ASTMD-790(3.2mm(0.125in),23℃(73℉))9600MPa
(3.2mm(0.125in),23℃(73℉))9600MPa
(0.8mm(0.032in),23℃(73℉))13900MPa
拉伸模量 (1.6mm(0.063in),23℃(73℉))11569MPaASTM D-638拉伸強(qiáng)度(1.6mm(0.063in),23℃(73℉))141MPaASTM D-638斷裂伸長率(1.6mm(0.063in),23℃(73℉))3.3%ASTM D-638壓縮模量4100MPaASTM D-695彎曲強(qiáng)度(3.2mm(0.125in),23℃(73℉))125MPaASTM D-790IZOD沖擊強(qiáng)度(3.2mm(0.126in))160J/mASTM D-256斷裂伸長率(3.2mm(0.125in),23℃(73℉))4%ASTM D-638拉伸模量
ASTM D-638(3.2mm)10500MPa
(1.6mm(0.063in),23℃(73℉))11569MPa
壓縮模量4100MPaASTM D-695彎曲強(qiáng)度 (0.8mm(0.032in),23℃(73℉))158MPaASTMD-790彎曲模量 (0.8mm(0.032in),23℃(73℉))13900MPaASTM D-790拉伸模量(3.2mm(0.125in),23℃(73℉))10500MPaASTM D-638IZOD沖擊強(qiáng)度(3.2mm(0.126in))160J/mASTM D-256彎曲強(qiáng)度(0.8mm(0.032in),23℃(73℉))158MPaASTM D-790拉伸強(qiáng)度(3.2mm(0.125in),23℃(73℉))125MPaASTM D-638電氣性能額定值單位測試方法損耗因數(shù)
ASTM D-2520B(0.8mm(0.032in),23℃(73℉))0.001
(1.6mm(0.063in),23℃(73℉))0.002
介電強(qiáng)度 (0.8mm)49Kv/mmASTM D-149介電常數(shù)
(0.8mm(0.032in),23℃(73℉))3.9
ASTM D-2520 B(0.8mm(0.032in))2.9
ASTM D-150(1.6mm(0.063in),23℃(73℉))4
ASTM D-2520 B損耗因數(shù) (0.8mm(0.032in))0.013
ASTM D-150介電強(qiáng)度 (3.2mm)26Kv/mmASTM D-149介電常數(shù)
(0.8mm)3.3
ASTM D-150(3.2mm(0.125in),23℃(73℉))4.1
ASTM D-2520 B(3.2mm(0.125in))3.6
ASTM D-150介電強(qiáng)度 (1.6mm)41Kv/mmASTM D-149損耗因數(shù)(1.6mm(0.063in),23℃(73℉))0.001
ASTM D-2520 B介電常數(shù) (3.2mm(0.125in))3.6
ASTM D-150損耗因數(shù)
ASTM D-150(0.8mm(0.032in))0.029
(0.8mm(0.032in))0.009
(3.2mm(0.125in))0.013
介電常數(shù) (0.8mm(0.032in))3.3
ASTM D-150表面電阻率>1×10OhmASTM D-257介電常數(shù)
ASTM D-2520B(3.2mm(0.125in),23℃(73℉))3.9
(0.8mm(0.032in),23℃(73℉))4.1
體積電阻率>1×10Ohm-cmASTM D-257損耗因數(shù)
ASTM D-2520B(0.8mm(0.032in),23℃(73℉))0.002
(3.2mm(0.125in),23℃(73℉))0.002
(3.2mm(0.125in),23℃(73℉))0.001
介電常數(shù)
(3.2mm(0.125in))3.2
ASTM D-150(1.6mm(0.063in),23℃(73℉))3.9
ASTM D-2520 B損耗因數(shù)
ASTM D-150(3.2mm(0.125in))0.028
加工性能額定值單位測試方法(3.2mm(0.125in))0.008
熱性能額定值單位測試方法熱變形溫度 (1.80MPa)239℃ASTM D-648玻璃化轉(zhuǎn)變溫度120℃ASTMD-3418模壓溫度范圍30-95℃
干燥溫度135℃
熔點335℃ASTM D-3418解鏈溫度范圍350-360℃
其它性能額定值單位測試方法工業(yè)含水量<0.01%
RTI,Electrical (1.5mm)130℃UL 746-BRTI,Mechanical with Impact(1.5mm)130℃UL 746-BRTI,Mechanical without Impact (1.5mm)130℃UL746-B